Debnáriková, Michaela ; Poláček, Petr (oponent) ; Bálková, Radka (vedoucí práce)
Master thesis deals with the influence of polyvinylacetate, polycaprolactone, poly(butylene-adipate-co-terephtalate) and talc, ethylenevinylacetate, polyethylene glycol and monosodium citrate on the flow properties, mechanical properties and crystallization ability of PLA. The flow properties were studied using the melt flow index and mechanical properties were studied using a tensile test. The crystallinity was studied by differential scanning calorimetry and on a polarization optical microscope equipped with hot stage. Isothermal crystallization was performed at 95 and 105 °C for 3 h and non-isothermal crystallization was performed with a calorimeter at two cooling rates (1 and 10 °C/min). Upon the isothermal crystallization at 95 °C, the formation of denser crystalline structure was observed and the content of crystalline phase increased in most of the samples. The formation of spherulitic structure was observed at 105 °C in samples with 30 % PVAc, 30 % EVA and PEG. Reducing the cooling rate to 1 °C/min at non-isothermal crystallization had nearly no effect on the crystallization process of the most samples; the content of crystalline phase increased in the samples containing PBAT and PEG, which revealed double melting peak during subsequent heating. The crystalline fraction was the most significantly affected by the addition of PEG. All added polymers except PVAc affected the mechanical properties; PBAT, PCL, EVA and PEG increased the strain and decreased the strength and modulus of elasticity. The samples containing monosodium citrate showed unsatisfactory mechanical properties and could not be measured. The samples containing higher concentration of EVA copolymer showed the phase separation.
|
|
|
Studium krystalické struktury polyhydroxybutyrátu a nukleační aktivity vybraných typů aditiv
Sedláček, Zbyněk ; Tocháček, Jiří (oponent) ; Bálková, Radka (vedoucí práce)
Diplomová práce se zabývá studiem krystalické struktury polyhydroxybutyrátu obsahujícího různé typy aditiv, které byly vybrané za účelem posouzení jejich nukleační aktivity, a které byly do matrice zahnětené. Jedná se o boronitrid (BN), sacharin, hydroxyapatit, plastifikátor Tegmer a tři druhy mastku. Krystalická struktura byla analyzovaná metodou diferenční kompenzační kalorimetrie a rentgenové difrakční analýzy, nadmolekulární struktura byla pozorovaná metodou optické mikroskopie (polarizační a konfokální laserová). Nukleační aktivita aditiv byla vyhodnocená z izotermické a neizotermické krystalizace provedené na kalorimetru a na vyhřívaném stolku optického mikroskopu. Přidaná aditiva nemají vliv na krystalografickou strukturu, ale ovlivňují počet a velikost vzniklých sférolitů včetně defektnosti krystalických domén, což se v konečném důsledku projeví na výsledných mechanických vlastnostech. Jako nukleační činidlo působí BN a mastek, ostatní aditiva nukleaci při nízkých a vysokých teplotách chlazení (vc) inhibují, při středních rychlostech se výrazně neprojevují. Nukleační aktivita není vyhodnocena číselně, protože pokles teploty krystalizace reference s vc není lineární. Výsledky nepřímých metod jsou podloženy obrazovou analýzou krystalické struktury, což je velkým přínosem pro porozumění krystalického chování PHB.
|
|
|
Crystallization of binary polylactide blends and their morphology
Debnáriková, Michaela ; Poláček, Petr (oponent) ; Bálková, Radka (vedoucí práce)
Master thesis deals with the influence of polyvinylacetate, polycaprolactone, poly(butylene-adipate-co-terephtalate) and talc, ethylenevinylacetate, polyethylene glycol and monosodium citrate on the flow properties, mechanical properties and crystallization ability of PLA. The flow properties were studied using the melt flow index and mechanical properties were studied using a tensile test. The crystallinity was studied by differential scanning calorimetry and on a polarization optical microscope equipped with hot stage. Isothermal crystallization was performed at 95 and 105 °C for 3 h and non-isothermal crystallization was performed with a calorimeter at two cooling rates (1 and 10 °C/min). Upon the isothermal crystallization at 95 °C, the formation of denser crystalline structure was observed and the content of crystalline phase increased in most of the samples. The formation of spherulitic structure was observed at 105 °C in samples with 30 % PVAc, 30 % EVA and PEG. Reducing the cooling rate to 1 °C/min at non-isothermal crystallization had nearly no effect on the crystallization process of the most samples; the content of crystalline phase increased in the samples containing PBAT and PEG, which revealed double melting peak during subsequent heating. The crystalline fraction was the most significantly affected by the addition of PEG. All added polymers except PVAc affected the mechanical properties; PBAT, PCL, EVA and PEG increased the strain and decreased the strength and modulus of elasticity. The samples containing monosodium citrate showed unsatisfactory mechanical properties and could not be measured. The samples containing higher concentration of EVA copolymer showed the phase separation.
|
|
|
Studium krystalické struktury polyhydroxybutyrátu a nukleační aktivity vybraných typů aditiv
Sedláček, Zbyněk ; Tocháček, Jiří (oponent) ; Bálková, Radka (vedoucí práce)
Diplomová práce se zabývá studiem krystalické struktury polyhydroxybutyrátu obsahujícího různé typy aditiv, které byly vybrané za účelem posouzení jejich nukleační aktivity, a které byly do matrice zahnětené. Jedná se o boronitrid (BN), sacharin, hydroxyapatit, plastifikátor Tegmer a tři druhy mastku. Krystalická struktura byla analyzovaná metodou diferenční kompenzační kalorimetrie a rentgenové difrakční analýzy, nadmolekulární struktura byla pozorovaná metodou optické mikroskopie (polarizační a konfokální laserová). Nukleační aktivita aditiv byla vyhodnocená z izotermické a neizotermické krystalizace provedené na kalorimetru a na vyhřívaném stolku optického mikroskopu. Přidaná aditiva nemají vliv na krystalografickou strukturu, ale ovlivňují počet a velikost vzniklých sférolitů včetně defektnosti krystalických domén, což se v konečném důsledku projeví na výsledných mechanických vlastnostech. Jako nukleační činidlo působí BN a mastek, ostatní aditiva nukleaci při nízkých a vysokých teplotách chlazení (vc) inhibují, při středních rychlostech se výrazně neprojevují. Nukleační aktivita není vyhodnocena číselně, protože pokles teploty krystalizace reference s vc není lineární. Výsledky nepřímých metod jsou podloženy obrazovou analýzou krystalické struktury, což je velkým přínosem pro porozumění krystalického chování PHB.
|